Process for producing semiconductor device

ABSTRACT

A process for producing a semiconductor device comprising the steps of: 
     (a) on a semiconductor Si substrate having a gate electrode formed thereon through the intermediary of an SiO 2  film, 
     i) forming as side wall of SiO 2  on the side of said gate electrode followed by formation of an SiN film over the entire surface of the Si substrate, or 
     ii) forming on the entire surface of said substrate, an SiO 2  film and and SiN film in sequence, followed by formation of a side wall of SiO 2  on the side of said gate electrode; 
     (b) injecting ions into said substrate; and 
     (c) subjecting said substrate to a heat treatment with or without removal of the side wall of SiO 2 , thereby forming a diffusion region in the substrate.

This is a continuation of application Ser. No. 07/658,345, filed 20 Feb. 1991, now abandoned.

BACKGROUND OF THE INVENTION

(1) Field of the Invention

The present invention relates to a process for producing a semiconductor device and, more particularly, to a process for producing a MOS type memory cell having a so-called LDD structure by forming a diffusion region on a silicon substrate using, as a mask, a gate electrode having a side wall.

(2) Description of the Related Art

FIGS. 6(a) to 6(f) show a typical conventional process for producing a MOS type memory cell. In this process, a polysilicon layer 43 as a gate material is formed on a Si substrate 41 through the intermediary of a gate oxide film 42. An NSG layer (non-doped silicate glass layer) 44 is formed as required on the polysilicon layer 43 for the purpose of improving the gate characteristic, as shown in FIG. 6(a). Then, a resist layer 45 is formed thereon. Subsequently, a wet etching is effected on a resist layer 45 so as to form this resist layer into a predetermined pattern for forming a gate electrode. Subsequently, a photo-etching is conducted to form a laminate structure composed of a gate electrode 49 having the polysilicon layer 43 and the NSG layer 44 and the resist layer 45, as shown in FIG. 6(a).

Then, after the removal of the resist layer 45, an SiO₂ layer 46a having a gate electrode 49 is formed on the Si substrate 41, as shown in FIG. 6(b), followed by an RIE (reactive ion etching) method for forming a side wall 46, as shown in FIG. 6(c).

In a subsequent step, As+ ions 47 are injected as shown in FIG. 6(d) while the gate electrode 49 and the side wall 46 are used as a mask, whereby an ion injected layer (not shown) is formed. Then, a heat-treatment is conducted to form a source-drain diffusion region 48 on the Si substrate 41 as shown in FIG. 6(e).

Then, a BPSG (boron-doped phospho-silicate glass) film 60 as an inter-layer insulating film is laminated on the entire area. Contact holes 50 are formed through the BPSG film so as to reach the diffusion region 48 and a metallic wiring 51 is laid to fill the contact holes 50, whereby a MOS type memory cell is formed as shown in FIG. 6(f).

This known process suffers from the following disadvantages. Namely, there is a risk that crystalline defects tend to be generated in the side wall edge portion 46b and in the diffusion region 48, as a result of injection of As+ ions 47 (see FIG. 6(d)) and/or the heat treatment (see FIG. 6(e)).

More specifically, the RIE method conducted for the purpose of forming the side wall 46 (see FIG. 6(c)) also damages the Si substrate. In the subsequent heat treatment, defects are produced around the damaged portions of the Si substrate since these damaged portions serve as nuclei. In addition, the side wall edge portion 46b forms a steep slope with respect to the surface of the Si substrate so that a large stress is incurred on the surface region of the Si substrate. As a consequence, the stress is transferred into the Si substrate through a subsequent heat treatment, with the result that a crystalline defect is formed in the Si substrate.

In addition, there is a risk that the BPSG layer 60 is diffused as impurities into the diffusion region 48 during formation of this film 60. This undesirably increases electrical leak in the products and reduces the yield of the products.

The following process has been proposed to overcome the above-described problems. In this proposed process an SiO₂ layer 63 is formed on a gate electrode 62 of a Si substrate 61 as shown in FIG. 7(a), followed by a combination of an RIE method and an HF etching method so that a side wall 51 is formed while leaving an SiO₂ film on the gate electrode 62, as shown in FIG. 7(b). According to this method, damaging of the Si substrate 61 due to RIE method is avoided. In addition, a taper 51a is formed by the residue of the SiO₂ film on the end of the side wall, thus relieving stress applied to the Si substrate. However, when ion injection is conducted on this laminate structure, oxygen is introduced into the Si substrate from the SiO₂ film formed thereon, so that a crystalline defect is formed in the diffusion layer formed by the heat treatment. More specifically, referring to FIG. 8, the defect density is small when the thickness of a SiO₂ film 64 ranges between 300 and 500 Å but is increased when the thickness is reduced, in case where the As+ ions are injected at an energy density of 80 KeV and a dosage 5×10¹⁵ cm⁻². In this process, however, the film thickness largely fluctuates because of use the RIE method for forming the side wall, so that it is not easy to control the film thickness to the above-mentioned restricted range. Thus, the SiO₂ film thickness below 300 A undesirably allows implantation of a large quantity of oxygen atoms from the SiO₂ film into the Si substrate, thus inducing generation of crystalline defects.

The current demand for larger scale of integration of semiconductor devices requires that the diffusion layer be formed to a smaller depth and with a high quality devoid of any defect. A process which employs a short heat treatment at high temperature subsequent to the ion injection of FIG. 6(d) is considered as being a promising process for obtaining such a thin diffusion layer of a high quality. According to this process, however, slip lines are liable to be formed around transfer loops which are generated during the heat-treatment and which function as nuclei, due to a rapid cooling which is essential in the short heat-treatment. More specifically, as shown in FIG. 9, defects tend to be generated in two stages: namely, in the interface S1 between the amorphous Si and the crystalline Si of the Si substrate 1 and in a region near the projection range (Pr) S2. In FIG. 9, S1a and S2a show defects which originate from transfer loops. In particular, the defect S1a generated in the deep interface S1 is liable to cause a leak in the diffusion layer.

The following reference is available as showing an art relevant to the invention of this application:

M. Tamura et al, Japanese Journal of Applied

Physics, 27(12), 2209-2217, 1988

SUMMARY OF THE INVENTION

The present invention provides a process for producing a semiconductor device comprising the steps of:

(a) on a semiconductor Si substrate having a gate electrode formed thereon through the intermediary of an SiO₂ film,

i) forming as side wall of SiO₂ on the side of said gate electrode followed by formation of an SiN film over the entire surface of the Si substrate, or

ii) forming on the entire surface of said substrate, an SiO₂ film and and SiN film in sequence, followed by formation of a side wall of SiO₂ on the side of said gate electrode;

(b) injecting ions into said substrate; and

(c) subjecting said substrate to a heat treatment with or without removal of the side wall of SiO₂ thereby forming a diffusion region in the substrate.

The process of the present invention can prevent the generation of crystalline defects which tend to be produced in the diffusion region of the Si substrate and in the side wall of the gate electrode material in the process for producing a semiconductor device having an LDD structure, while enabling formation of a diffusion region of a small depth and fewer defects, while coping with the demand for larger scales of integration of the semiconductor device. As a consequence, electrical leakage in the semiconductor device is reduced to improve the yield of products.

The invention also provides a process for producing a semiconductor device having the steps of: preparing a semiconductor substrate having a gate electrode formed thereon through the intermediary of an SiO₂ film, forming a side wall of SiO₂ on the side of the gate electrode, effecting an ion injection with a low acceleration energy, conducting a heat treatment at a low temperature, and conducting a short heat treatment at a high temperature thereby forming a diffusion region. According to the invention, it is possible to obtain a diffusion region with a small depth and reduced defects.

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1(a) to 1(f) are illustrations of steps of an embodiment of the process of the present invention;

FIGS. 2(a) to 2(f) are illustrations of steps of another embodiment of the process of the present invention;

FIGS. 3(a) to 3(c) are illustrations of steps of still another embodiment of the process of the present invention;

FIG. 4 is a graph showing the relationship between the density of defects in an Si substrate and the energy level of ion injection, wherein A represents the interface between the amorphous phase and crystalline phase of Si in the Si substrate, and B shows the above-mentioned relationship in the projection range;

FIG. 5 is a graph showing the relationship between a lamp annealing temperature and the sheet resistance and the relationship between the lamp annealing temperature and the depth of a diffusion region;

FIGS. 6(a) to 6(f) and FIGS. 7(a) to 7(b) are illustrations of known processes;

FIG. 8 is a graph showing the relationship between the thickness of the SiO₂ film and the density of defects in an Si substrate;

FIG. 9 is an illustration of locations of defects generated in an Si substrate; and

FIG. 10 is a graph showing the relationship between the SiN/SiO₂ film thickness ratio and the density of defects in an Si substrate.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

According to the present invention, a side wall of SiO₂ can be formed on the side of a gate electrode by depositing an SiO₂ film using a CVD method followed by etching using preferably the combination of an RIE method and an HF etching method.

Examples of ions to be used in the ion injection are As⁺ ions, BF₂ ⁺ ions or the like.

When the formation of the SiN film in the step (a) i) of the process of the invention is effected by a CVD method while the heat treatment in the step (c) is effected without removal of the side wall, it is preferred that the SiN film has a thickness of 100 Å to 300 Å and the ion injection is conducted at an acceleration energy level of about 40 to 90 KeV and a dosage of about 3 to 5×10¹⁵ cm⁻², while the heat treatment is preferably conducted at a temperature ranging between about 800° and 900° C.

According to the method, the knock-on effect of oxygen atom upon ion injection can be avoided and the growth of transfer loops can be prevented.

When the process of the present invention is carried out such that the formation of the SiO₂ film and the formation of the SiN film in the step (a) ii) are effected by a heat oxidation method and a CVD method, respectively, while the heat-treatment in the step (c) is effected after removal of the side wall, it is preferred that the thickness of the SiO₂ film and SiN film preferably ranges between about 50 and 150 Å and that the ion injection is conducted with an acceleration energy of 40 to 90 KeV and at a dosage of about 3 to 5×10¹⁵ cm⁻², while the heat treatment is preferably conducted at a temperature of about 800° to 900° C.

According to this method, since the ions are injected through the SiO₂ film and the SiN film, implantation of the oxygen atoms from the SiO₂ film into the Si substrate can be diminished. In addition, an implantation of nitrogen atom from the SiN film into the Si substrate is extremely small. Furthermore, the etching during forming the side wall is stopped by the SiN film so that the thickness control of the SiO₂ film and the SiN film is facilitated and qualities of these films can be improved. Consequently, defective crystals in the diffusion region produced by the heat treatment can be diminished.

When the process of the present invention is carried out in such a manner that the formation of the SiO₂ film and the formation of the SiN film in the step (a) ii) are effected by a heat-oxidation method and a nitriding method, respectively, while the heat-treatment in the step (c) is conducted after removal of the side wall, it is preferred that the SiO₂ film has a thickness of about 50 to 150 Å and the SiN film has a thickness of about 5 to 15 Å, and that the ion injection is conducted with a low acceleration energy of 20 to 50 KeV and a dosage of about 3 to 5×10¹⁵ cm⁻², while the heat-treatment is preferably conducted at a temperature of about 800° to 900° C.

According to this process, the implantation of oxygen atom from the SiO₂ film and nitrogen atom from the SiN film into the Si substrate can be reduced, so that the thickness control of the SiO₂ film and the SiN film is facilitated and these films can be improved on quality. Consequently, defective crystals in the diffusion region produced by the heat treatment can be diminished. Furthermore, the depth of the diffusion region is reduced because the acceleration energy with which the ion injection is conducted can be reduced.

When the process of the present invention is carried out such that a side wall of SiO₂ is formed on the side of the gate electrode while the ion injection is conducted with a low acceleration energy followed by a low-temperature heat treatment and a subsequent short heat-treatment at a high temperature, it is preferred that the ion injection is conducted with a low acceleration energy level of about 10 to 20 KeV and at a dosage of about 2 to 5×10¹⁵ cm⁻², and that the low-temperature heat-treatment is effected at about 700° to 850° C. while the short heat-treatment is conducted for 5 to 15 seconds at about 900° to 1100° C.

According to the method of the present invention, the crystallinity of the ion injection layer formed by the low-energy ion injection is recovered by the low-temperature heat treatment, while the subsequent short heat-treatment at high temperature provides a high activated rate of the diffusion region with a reduced defects. Furthermore, the depth of the diffusion region can be reduced by virtue of the low acceleration level employed in the ion injection.

Preferred embodiments of the present invention will be described only for an illustrative purpose. Thus, the described embodiments ar not intended for limiting the scope of the invention.

FIRST EMBODIMENT

As shown in FIG. 1(a), a gate electrode 34 composed of a polysilicon layer 3 and an NSG layer 4 is formed on an Si substrate 1 through the intermediary of an SiO₂ film 2, and a resist layer 5 is laminated on the gate electrode 34. Namely, the gate oxide film 2, the polysilicon layer 3, the NSG layer 4 and the resist layer 5 are formed in sequence on the Si substrate 1 by a known process. Subsequently, a wet etching process is executed to patternize the resist layer into a predetermined pattern for forming the gate electrode. Subsequently, an RIE method is conducted so that a laminate structure as shown in FIG. 1(a) is obtained.

In a next step, the resist layer 5 is removed by a known method and an HTO (high temperature oxide) film (SiO₂ layer) 6a is formed in a thickness of 3800 Å under reduced pressure as shown in FIG. 1(b). Then, an RIE method and an HF etching method are executed to etch the laminate structure until the Si substrate 1 is exposed, thus forming a tapered sidewall 6. Then, CVD method is conducted under reduced pressure so as to laminate an SiN film 9 in a thickness of 200 Å, as shown in FIG. 1(c).

Then, as shown in FIG. 1(d), injection of As⁺ ions 7 is conducted while using the laminate of the gate electrode 34 and the side wall 6 as a mask, at an acceleration energy level of about 80 KeV and a dosage of 1×10¹⁵ to 1×10¹⁶ cm⁻², thus forming the ion injection layer (not shown).

Subsequently, a heat-treatment is effected at 800° to 900° C. so that a source-drain diffusion region 10 is formed in the Si substrate as shown in FIG. 1(e).

Then, ordinary steps are taken so as to form a MOS type memory cell. Namely, after laminating a BPSG film 13 as an inter-layer insulating film over the entire area, an annealing is conducted in an N₂ gas atmosphere so as to flatten this layer. Subsequently, contact holes 11 are formed to reach the diffusion region 10, and a metallic wiring 12 is laid to fill these contact holes, whereby the MOS type memory cell is completed.

According to the first embodiment of the process as described, after the formation of the side wall the SiN film is formed over the entire area, so that the knock-on effect of oxygen atom is eliminated and the growth of transfer loops which occurs upon the heat treatment is completely prevented. Furthermore, diffusion of impurities from the BPSG film also is prevented. As a consequence, the electric characteristics of the product device are stabilized to improve the yield of products.

SECOND EMBODIMENT

Referring to FIG. 2(a), a semiconductor substrate 21 is produced which has a gate electrode 23 made of a gate material polysilicon on the substrate surface through the intermediary of an SiO₂ film 22, as in the case of the first embodiment.

Subsequently, an SiO₂ film 22a is formed over the entire area of the gate electrode 23 and the Si substrate 21 to have a thickness of 100 Å by a heat-oxidation process conducted under normal pressure. Then, on the SiO₂ film 22a, an SiN film of 100 Å thick is formed by CVD process conducted under reduced pressure, as shown in FIG. 2(b).

Then, an HTO film (SiO₂ film) 25a for forming an side wall is laminated on the SiN film 24 as shown in FIG. 2(c).

Then, the HTO film 25a is etched by an RIE method and an HF etching method until the SiN film 24 is exposed, whereby a side wall 25 is formed only on the peripheral side of the gate electrode as shown in FIG. 2(d).

Subsequently, injection of As⁺ ions is conducted under conditions of 80 KeV and 5×10¹⁵ cm⁻², by using the side wall 25, SiN film 24 and the SiO₂ film as a mask, whereby an ion injection layer (not shown) is formed.

Then, an RIE method and an HF etching method are executed so as to remove the side wall 25, and a phosphate boiling process is executed for removing the SiN film 24, followed by a heat-treatment conducted at 800° to 900° C., whereby a laminate structure having a diffusion region 26 is obtained as shown in FIG. 2(e).

Then, as in the case of the first embodiment, an interlayer insulating film 27 is formed over the entire area and an N₂ annealing is conducted to flatten this film 27. Finally, contact holes 28 are formed and a metallic wiring 29 is laid to fill these contact holes, thus completing a MOS type memory cell as shown in FIG. 2(f).

In the second embodiment as described, the thickness d₁ of the SiN film and the thickness d₂ of the SiO₂ film are suitably determined such that the total thickness d (=d₁ +d₂) of these films ranges from about 200 Å to about 400 Å. Preferably, these thicknesses are determined to simultaneously meet the condition of d₁ ≧d₂ and d₂ >50 Å. The relationship between the defect density in the diffusion region and the thickness ratio d₁ /d₂ as obtained when As⁺ ions are injected is shown in FIG. 10.

THIRD EMBODIMENT

A diffusion region was formed in the same manner as the second embodiment except that an SiN film of about 10 Å in thickness was formed by effecting a lamp annealing on the SiO₂ film in an ammonia gas atmosphere at 900° to 1000° C. and that injection of As⁺ ions was effected with a low acceleration energy level of 40 KeV and a dosage of 5×10¹⁵ cm⁻². As a consequence, a diffusion region was formed to have a small depth of about 1000 Å with reduced generation of defective crystals.

FOURTH EMBODIMENT

As shown in FIG. 3(a), an Si substrate 31, having a gate electrode 33 formed of a polysilicon layer through the intermediary of an SiO₂ film 32, was prepared in the same manner as the second embodiment, followed by a lamination with an SiO₂ layer 36a by an HTO method as shown in FIG. (3b). Subsequently, an etching was effected by an RIE method and a HF etching method until the gate electrode 33 is exposed so as to form a side wall 36 on the peripheral side of the gate electrode. Then, As⁺ ions were injected with a low acceleration energy of 20 KeV and a dosage of 5×10¹⁵ cm⁻² so as to form an ion injection layer of about 1000 Å as shown in FIG. 3(c). Subsequently, a low-temperature heat-treatment was conducted at 800° C. for 1 hour in a nitrogen atmosphere. The crystallinity was recovered from a disordered state caused by the ion injection, thanks to the low level of the acceleration energy employed in the ion injection, as will be clearly seen from FIG. 4. It is thus understood that the use of a low level acceleration energy in the ion injection reduces the density of defect in the interface (line A in FIG. 4) between the amorphous and crystalline phases of Si and in the projection range (line B in FIG. 4). Then, a short heat-treatment at high temperature was conducted at 1000° C. for 10 seconds so that a diffusion region of a small depth was obtained, as will be seen from FIG. 5. More specifically, it will be understood that the sheet resistance is reduced when the temperature of the short heat-treatment is elevated. For instance, a low level of resistance not higher than 50Ω/□ is obtained when this heat-treatment is effected at 1000° C. and the depth of the diffusion region is maintained substantially constantly at 1000 Å when the temperature of this heat-treatment is below 1000° C. 

What is claimed is:
 1. A process for producing a semiconductor device comprising the steps of:(a) on a semiconductor Si substrate having a gate electrode formed thereon through the intermediary of an SiO₂ film, forming on the entire surface of said substrate including said gate electrode, an SiO₂ film and a SiN film in sequence, followed by formation of a side wall of SiO₂ on the side of said gate electrode, the formation of the SiO₂ film being conducted by a heat oxidation method and the formation of the SiN film being conducted by a nitriding method; (b) injecting ions into said substrate through said SiO₂ film and said SiN film formed in sequence; and (c) removing the side wall of SiO₂, followed by removal of the SiN film, the ion injection being conducted at an acceleration energy level of 20 KeV to 50 KeV and a dosage of about 3 to 5×10¹⁵ cm⁻² ; and, (d) subjecting said substrate to heat treatment to form a diffusion region therein.
 2. The process of claim 1 wherein the SiO₂ film has a thickness of about 50 Å to 150 Å and the SiN film has a thickness of about 5 Å to 15 Å.
 3. The process of claim 1 wherein the ion injection is conducted so as to inject As⁺ ions.
 4. The process of claim 1 wherein the formation of said side wall of SiO₂ is conducted utilizing an RIE method and an HF etching method.
 5. The process of claim 1 wherein the heat treatment is conducted at about 800° C. to 900° C.
 6. A process for producing a semiconductor device comprising the steps of:(a) on a semiconductor Si substrate having a gate electrode formed thereon through the intermediary of an SiO₂ film, forming on the entire surface of said substrate, an SiO₂ film and SiN film in sequence, followed by formation of a side wall of SiO₂ on the side of said gate electrode; (b) injecting ions into said substrate; and (c) subjecting said substrate to a heat treatment, thereby forming a diffusion region in the substrate; whereinin step (a) the formation of the SiO₂ is conducted by a heat oxidation method and the formation of the SiN film is conducted by a nitriding method, in step (b) the ion injection is conducted at an acceleration energy level of 20 KeV to 50 KeV and a dosage of about 3 to 5×10¹⁵ cm⁻².
 7. A process as in claim 6 wherein the heat treatment is conducted with removal of the side wall of SiO₂.
 8. A process as in claim 6 wherein the SiO₂ film has a thickness of about 50 Å to 150 Å and the SiN film has a thickness of about 5 Å to 15 Å. 